EPO-TEK® 310M Black
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8seT7I_EPO-TEK-310M-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, flexible, optically opaque epoxy adhesive designed for optical, semiconductor and medical applications. Replacement for EPO-TEK® 310 Black. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | < 15.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 7.8E-5 | cm/cm/°C | |
| -- 3 | 2.6E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance | |||
| 400 to 1000 nm | < 7.0 | % | |
| 1000 to 1550 nm | < 15.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 5.5 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 397 | °C | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 5.01 | MPa | |
| Weight Loss on Heating | |||
| 200°C | 0.090 | % | |
| 250°C | 0.28 | % | |
| 300°C | 0.64 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Black | ||
| -- 5 | Clear/Transparent | ||
| Density | |||
| Part B | 1.08 | g/cm³ | |
| Part A | 1.11 | g/cm³ | |
| Viscosity 6(23°C) | 0.45 to 0.85 | Pa·s | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 120 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 69 | ||
| Lap Shear Strength (23°C) | 2.44 | MPa | |
| Relative Permittivity (1 kHz) | 6.62 | ||
| Volume Resistivity (23°C) | > 1.0E+10 | ohms·cm | |
| Dissipation Factor (1 kHz) | 1.1 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LS00715 - A | Premier Polymers, LLC. | LLDPE | Premier |
| Precision Polymer E81H | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| Cellophane™ 320DM | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| CYCOLAC™ DL200H resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Lupoy® GN5001RFH | LG Chem Ltd. | PC+ABS | Lupoy® |