Plexar® PX3227
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8rT3d1_Plexar-PX3227.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.913 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 8.80 | MPa | |
| TD : Yield, 51 µm, Blown Film | 9.70 | MPa | |
| MD : Break, 51 µm, Blown Film | 28.7 | MPa | |
| TD : Break, 51 µm, Blown Film | 22.1 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 30 | % | |
| TD : Yield, 51 µm, Blown Film | 12 | % | |
| MD : Break, 51 µm, Blown Film | 840 | % | |
| TD : Break, 51 µm, Blown Film | 840 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, Blown Film | 270 | g | |
| TD : 51 µm, Blown Film | 590 | g | |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 5.6 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | > 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT3080-757UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| VESTOSINT® 2178 white | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| Witcom PPS 6C/3L3-L | Witcom Engineering Plastics B.V. | PPS, Linear | Witcom PPS |
| NuSil MED-4055 | NuSil Technology | Rubber | NuSil |
| Evermore PUR UP-9321N | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |