Tecopet® PT70 GR30 NL100 HT
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecopet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ptmT5_Tecopet-PT70-GR30-NL100-HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET, 30% glass fiber reinforced, high heat stabilized, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.90 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.080 | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 225 | °C | ISO 306/B |
| Melting Temperature 1 | 255 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 50.0 to 70.0 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 to 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN JHC-374 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| TITANEX® HB0972 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANEX® |
| VITAMIDE® BF13BL6555 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Xuchuan XCW-8015 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NOVADURAN® SEF-530 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |