POLIMAXX 1111NXTA8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | IRPC Public Company Limited |
| Trademark: | POLIMAXX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8plGOl_POLIMAXX-1111NXTA8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 1111NXTA8 is a PP Homopolymer with 40% talcum filler for injection molding process, medium melt flow, high flexural modulus and high heat resistance. It is suitable for auto parts and electrical appliances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 584 mm) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 35.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7350 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 54.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 2.16 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 147 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2090-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Niuk YPC6008 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| BLUESTAR® 1100 | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| DynaPath™ 3225-SS | Polymer Dynamix | PEEK | DynaPath™ |
| PEARLSTICK® 45-50/29 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |