Fiberfil® J-68/25/E/SD
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8pf1qu_Fiberfil-J-68-25-E-SD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-68/25/E/SD is a polypropylene copolymer (PP Copoly) material, which contains a 25% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-68/25/E/SD are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 - 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.15 - 0.30 | % | ASTM D955 |
| 6.35 mm | 0.25 - 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3620 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 7.5 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 3500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 8203 | Borealis AG | Plastomer | Queo™ |
| Brush-On® 60 | Smooth-On, Inc | PUR, Unspecified | Brush-On® |
| Daelim Po1y® LD-41 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| Leona™ 53G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Lucel® N145LD | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |