Order Products : sales@su-jiao.com
Novalloy-S S4230 (type V)
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8pWtGM_Novalloy-S-S4230-type-V-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S4230 (type V) is a Polycarbonate + ABS (PC+ABS) material filled with 30% glass fiber. It is available in Asia Pacific. Primary attribute of Novalloy-S S4230 (type V): Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 92.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7700 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 123 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 116 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 26 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 69.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 4 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 100 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 149 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 300 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 150 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 200 to 240 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2000-75A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TORZEN® U5101 NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| NYCOA Polyamide 4212 HS | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| DIC.PPS Z-240 | DIC Corporation | PPS | DIC.PPS |
| Exelene® PS 6900 | Montachem International, Inc. | PS (GPPS) | Exelene® PS |