Flexirene® FG 20 I
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Flexirene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8pWlPR_Flexirene-FG-20-I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexirene FG 20 I is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion. Main Application Flexirene FG 20 I is recommended for the production of general purpose film, in blend or coextrusion with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 15 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 140 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 160 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 550 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 25.0 | kN/m | |
| TD : 25.0 µm | 170.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 100 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 10 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® T320C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| apilon 52® 7013 | API SpA | TPU-Polyester | apilon 52® |
| DOMAMID® 6GM404 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| LNP™ LUBRICOMP™ RFN18SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Polyfast SA001 | Ravago Group | ASA | Polyfast |