AKROMID® A3 K1 FR natural (2312)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8pGWpG_AKROMID-A3-K1-FR-natural-2312-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 K1 FR natural (2312) is a 25% glass fibre reinforced, halogenfree flame retardant polyamide 6.6 with light inherent color, all color listed at UL and NF F 16-101. Applications are switch housings in the electric industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.30 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 221 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9200 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 65 | 70 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength (3.00 mm) | 28 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | -- | % | ISO 4589-2 |
| Burning and Smoke Gas Classification | I3/F1 | -- | NF F16-101 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LGSTRENE LGH 310 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGSTRENE |
| Plexiglas® Diffuse V045-68194 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 8200-90 Clear Blue 8357 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Telcar® TL-2417J NAT | Teknor Apex Company | TPE | Telcar® |
| Sylvin 9812-60 Grey 9562 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |