PRL PPX-SF2
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8odwMr_PRL-PPX-SF2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-SF2 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by structural foam molding and is available in North America. Typical application: Foam. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 25 to 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 52.4 | MPa | |
| Break, 3.18 mm | 51.7 | MPa | |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 98.9 | °C | |
| RTI Elec | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 5.99 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 5.99 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 5.99 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | V-0 | ||
| 6.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® GF8001 | Covestro - Polycarbonates | PC | Makrolon® |
| TIPPLEN® H 949 A | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| TRIBOFORCE® PA66 C0200 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | TRIBOFORCE® |
| NEXUS Reprocessed ABS 8/3 RBK | Nexus Resin Group, LLC. | ABS | NEXUS Reprocessed |
| TECHNYL® A 216 V30 BLACK FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |