Infino CF-1030
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8nY4iw_Infino-CF-1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino CF-1030 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 28 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 56.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 73 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2200 | MPa | ASTM D790 |
| -- 3 | 2380 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 78.0 | MPa | ASTM D790 |
| -- 5 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 80 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 780 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 590 | J/m | ASTM D256 |
| 23°C 7 | 70 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 137 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.981 to 2.94 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 6200B | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| NEFTEKHIM PP 1425J (T28C) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Braskem PP PRISMA 6410 | Braskem | PP Random Copolymer | Braskem PP |
| POLYfill PPH GF5020 PD2 VT2 | Polykemi AB | PP Homopolymer | POLYfill |
| Sylvin 8773-60D White 1430 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |