3M™ Dyneon™ Fluoroelastomer E-20575
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ Fluoroelastomer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8n3ZvY_3MDyneonFluoroelastomerE20575.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
3M™ Dyneon™ Fluoroelastomer E-20575 is an ultra low viscosity (ULV) fluoroelastomer. E-2055 is an experimental product that has not been introduced or commercialized for general sale. It is a 65.9 % fluorine containing, peroxide curable dipolymer. This product offers excellent flow compared to conventional fluoroelastomers used in many difficult moulding applications. Special Features
Typical Applications Potential applications for Dyneon E-20575 range from moulding complex shapes to high solid sealants and coatings or viscosity modification of higher viscosity elastomers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | Internal method |
| Mooney Viscosity (ML 1+10, 100°C) | 4 | MU | Internal method |
| Fluorine Content | 66 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A 1 | 67 | ASTM D2240 | |
| Shaw A 2 | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain 3 | 4.10 | MPa | ASTM D412 |
| 100% strain 4 | 4.80 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| -- 5 | 14.4 | MPa | ASTM D412 |
| -- 6 | 17.7 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture 7 | 250 | % | ASTM D412 |
| Fracture 8 | 220 | % | ASTM D412 |
| Compression Set | ASTM D395B | ||
| 200°C, 22 hr 9 | 36 | % | ASTM D395B |
| 200°C, 70 hr 10 | 46 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | -20.0 | °C |
| Note Message | |
|---|---|
| 1 . | Press Cured 5' @ 177°C |
| 2 . | Post Cured 4 hours @ 232°C |
| 3 . | Press Cured 5' @ 177°C |
| 4 . | Post Cured 4 hours @ 232°C |
| 5 . | Press Cured 5' @ 177°C |
| 6 . | Post Cured 4 hours @ 232°C |
| 7 . | Press Cured 5' @ 177°C |
| 8 . | Post Cured 4 hours @ 232°C |
| 9 . | Press Cure Only |
| 10 . | Post Cure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 15 HI H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Ultramid® B3ZG6 | BASF Corporation | Nylon 6 | Ultramid® |
| KumhoSunny PC/ABS HAC8250NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| PENTAMID L GV30 H natur | PENTAC Polymer GmbH | Nylon 12 | PENTAMID L |
| Plexiglas® V825 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |