Ultramid® 8270 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8mlkWY_Ultramid-8270-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents. Applications Ultramid 8270 HS is generally recommended for applications such as industrial containers, small gasoline tanks, and automotive under hood reservoirs. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.6 | -- | % | |
| Saturation | 9.2 | -- | % | |
| Equilibrium, 50% RH | 2.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 138 | 119 | MPa | |
| Yield, 23°C | 84.0 | 46.0 | MPa | |
| Yield, 121°C | 24.0 | -- | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield, 23°C | 4.0 | -- | % | |
| Break, 23°C | > 100 | -- | % | |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 3160 | 3900 | MPa | |
| 23°C | 2900 | 760 | MPa | |
| 65°C | 435 | -- | MPa | |
| 90°C | 310 | -- | MPa | |
| 121°C | 260 | -- | MPa | |
| Flexural Strength | ASTM D790 | |||
| -40°C | 179 | 176 | MPa | |
| 23°C | 114 | 37.0 | MPa | |
| 65°C | 30.0 | -- | MPa | |
| 90°C | 20.0 | -- | MPa | |
| 121°C | 17.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 53 | 48 | J/m | |
| 23°C | 53 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 169 | -- | °C | |
| 1.8 MPa, Unannealed | 63.0 | -- | °C | |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 1.4E-4 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 6.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 6.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 6.00 mm | 65.0 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 6.00 mm | V-2 | -- |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Blow Molding Drying Temperature | 80 | -- | °C | |
| Blow Molding Drying Time | 2.0 to 4.0 | -- | hr | |
| Blow Molding Melt Temperature | 245 to 260 | -- | °C | |
| Blow Molding Moisture Content | < 0.15 | -- | % | |
| Blow Molding Mold Temperature | 60 | -- | °C | |
| Blow-up Ratio | 2:1 | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2002-4 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| RTP 1000 Z | RTP Company | PBT | RTP |
| TUFNYL® RXXIC INDICA GREY | SRF Ltd. | Nylon 66 | TUFNYL® |
| Yuyao PET PETG10 (FR) | Yuyao Tenglong Plastics Co., Ltd. | PET | Yuyao PET |
| Capran® 526 | Honeywell | Nylon, Unspecified | Capran® |