RAMOFIN PPC371B50
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8mdSvX_RAMOFIN-PPC371B50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% MINERAL FILLED, HEAVY DENSITY POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.1 to 1.4 | % | |
| -- | 1.1 to 1.4 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 15.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 28.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C | 6.0 | kJ/m² | ISO 180 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 230 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 70.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 387 TFE 15 | RTP Company | PC | RTP |
| NuSil CV16-2500 | NuSil Technology | Silicone | NuSil |
| Fainplast PVC FK 70/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ferro PP NPP00GC26NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Latiohm 88/10-06 CNT | LATI S.p.A. | PEEK | Latiohm |