LNP™ COLORCOMP™ DX06407H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8mHyDX_LNP-COLORCOMP-DX06407H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP DX06407H is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare Also known as: LNP* COLORCOMP* Compound D-1000 EM MR HC Product reorder name: DX06407H |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2350 | MPa | ASTM D638 |
| -- | 2310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/5 |
| Break 3 | 58.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.2 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2/5 |
| Break 5 | 94 | % | ASTM D638 |
| Break | 100 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2290 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 780 | J/m | ASTM D256 |
| 23°C 8 | 9.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 9 | 220 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 63.0 | J | ASTM D3763 |
| -- | 69.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 94.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 96.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 104 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 250 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| EPO-TEK® OG603 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KYDEX® FST | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| IROGRAN® A 70 E 4675 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Sumiliteresin® PR-50590 BI | SBHPP | Phenolic | Sumiliteresin® |