NAXALOY® 770PG
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXALOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8lm0bs_NAXALOY-770PG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Integrally Colored Resin. Further information and details are available upon request. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 51.7 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Instrumented Dart Impact (-29°C) | 50.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 271 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 260 - 282 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 60.0 - 82.2 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Cushion | 3.30 - 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 to 75% of injection pressureHold: 40 to 60% of injection pressureAir Flow Rate: 0.8-1.0 CFM per lb/hour resin processed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6PAN (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TIPELIN® 7111S | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| Adell PBT HT-16 | Adell Plastics, Inc. | PBT | Adell PBT |
| LUVOCOM® 16/XCF/25 | Lehmann & Voss & Co. | PARA | LUVOCOM® |
| Pearlthane® CLEAR 15N80 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |