DENITER 3010
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Vamp Tech |
| Trademark: | DENITER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8leihn_DENITER-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 12 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648A |
| Vicat Softening Temperature | 210 | °C | ASTM D1525 1 |
| RTI Elec | 135 | °C | UL 746 |
| RTI Imp | 135 | °C | UL 746 |
| RTI Str | 135 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANLON A 6005B UV | Polykemi AB | ABS+Nylon | SCANLON A |
| Unilex™ UP 9008 | United Polychem | PP Impact Copolymer | Unilex™ |
| Next Nylon 66 Prime Series PGHSLR33-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Novalloy-S S4210 (TypeV) | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| Cellophane™ 340XSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |