RALUPOL® UP 8605
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RALUPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8kyT6q_RALUPOL-UP-8605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass-fibre reinforced Polyester moulding compound Resistant to hydrolysis This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 to 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.95 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.40 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.30 | % | ISO 62 |
| Post Shrinkage 2 | < 0.10 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 210 | °C | |
| 20,000 h | 170 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 6000 to 8000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 70.0 to 100 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 15000 to 20000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 120 to 140 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.5 to 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 10 to 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | > 200 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.0E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.90 to 1.1 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 to 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 to 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm, Tested by RASCHIG) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A121U GR30-50 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| Nylene® 734 | Custom Resins Group | Nylon 6 | Nylene® |
| Chemlon® 66GF35 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Durolon® HFR1900 CR010 | Unigel Plásticos | PC | Durolon® |
| PIVINEL™ BK-1 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |