DOW™ LDPE 959S
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8kvh2t_DOW-LDPE-959S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOW Polyethylene 959S Low Density Resin is a medium molecular weight distribution homopolymer. This resin has good processability over a wide range of molding conditions. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 55 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | < 1.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 48 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 11.0 | MPa | ASTM D638 |
| Fracture | 6.21 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 58 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 331 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 118 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 46.1 | °C | ASTM D648 |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 110 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 100 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 GF 10 GB 20 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| CABELEC® CA4918 | Cabot Corporation | LDPE | CABELEC® |
| Karina BROWN COLOR CONCENTRATE 36/234-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ UX03320 compound | SABIC Innovative Plastics | PPA | LNP™ VERTON™ |
| NORYL™ GFN2F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |