KEY FEATURES

Uma PET HQ is transparent film with one side co-extruded layer of specially modified copolymer.

HQ film possesses low Haze, high clarity, high gloss along with good frictional, mechanical and thermal properties.

The Film can be used for direct contact with food and complies with FDA regulation 21CFR177.1630 sections (f) and (g).

APPLICATIONS

The modified co-extruded surface has excellent adhesion with water and solvent based inks, adhesives, release coatings, Varnishes, primers and Al-metals in metallization, resulted higher bond strength in final laminates.

Laminates with HQ film shows excellent inter layer bond strength retention in high end packaging applications like hot fill, boiling, retorting etc.

Boil in Bag, Doy-Pack type of packaging applications for various products.

General Information
Features	Bondability Food Contact Acceptable Good Strength High Clarity High Gloss Low Friction Salt Water/Spray Resistant
Uses	Film Laminates Packaging
Agency Ratings	FDA 21 CFR 177.1630 Sections (f) & (g)
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction ¹			ASTM D1894
vs. Itself - Dynamic	0.45
vs. Itself - Static	0.50

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12	µm
Film Thickness - Recommended / Available	12 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	206	MPa
TD : Break, 12 µm	216	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	100	%
TD : Break, 12 µm	90	%
Yield (12.0 µm)	59.5	m²/kg	Internal Method

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Functional side : 12.0 µm	42	dyne/cm
Plain side : 12.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze (12.0 µm)	3.0	%	ASTM D1003

Note Message
1 .	12 µm

Resin Grade	Manufacturer	Category	Trademark
SABIC® HDPE CC1053	Saudi Basic Industries Corporation (SABIC)	HDPE	SABIC® HDPE
Stat-Tech™ PC-15CF/000 FC BLACK	PolyOne Corporation	PC	Stat-Tech™
Karina BLACK PVC COMPOUND 75930-48/ 1-F-AC-LF	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Telcar® TL-2934F	Teknor Apex Company	TPE	Telcar®
NORYL™ LS6010 resin	SABIC Innovative Plastics	PPE+PS	NORYL™