Sindustris PBT TE5007F
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8iet7s_Sindustris-PBT-TE5007F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT TE5007F is a Polycarbonate + PBT (PC+PBT) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PBT TE5007F are:
Typical application of Sindustris PBT TE5007F: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| Peak Melting Temperature | 250 | °C | ASTM D3418 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.500 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.00 mm | V-0 5VA | ||
| 1.60 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPMI20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| Vi-Chem PVC V148-85 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Grivory® XE 5106 (GVL-4H V0) | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| LG PMMA IF860 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Sylvin 9915-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |