Carbo-Rite™ B-980
| Category: | PC , Polycarbonate |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Carbo-Rite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8iGNGt_Carbo-Rite-B-980.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbo-Rite™ B-980 is a reinforced Polycarbonate compound with carbon powder added for electrical consistency. Carbo-Rite™ B-980 solves a wide range of electronic handling problems through consistent dimensional stability and ESD performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 76.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4310 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 47 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 137 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | < 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity 2 | < 1.0E+4 | ohms·cm | ASTM D257 |
| Static Decay - 1000 V to 10 V 3 | < 0.1 | sec |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | < 0.00400 | ng/cm² | |
| Anions NO3- | < 0.00400 | ng/cm² | |
| Anions PO4- | ND | ||
| Anions SO4- | < 0.00400 | ng/cm² | |
| Outgassing | Internal Method | ||
| Hydrocarbon | 0.0740 | µg/g | |
| Phenol/Alcohol | ND | ||
| Siloxanes | ND | ||
| Total Organics | 0.0740 | µg/g |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 50% RH |
| 3 . | Charged Plate Monitor |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6010 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| TARFLON™ URC2501 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Alathon® L5485 | LyondellBasell Industries | HDPE, MMW | Alathon® |
| ALTECH® ABS A 1000/568.02 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| Kareline® PLMS6040 | Plasthill Oy | PLA | Kareline® |