Sindustris PC HI1003ML
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8iElkb_Sindustris-PC-HI1003ML.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC HI1003ML is a Polycarbonate (PC) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC HI1003ML are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 130 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 200 | J/m | |
| 23°C, 3.20 mm | 740 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 130 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 275 to 290 | °C | |
| Middle Temperature | 285 to 305 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP602N | PolyMirae | PP Homopolymer | Moplen |
| PEARLSTICK® D40-70/18 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |
| Sylvin 8480-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ICORENE® 1761 V2 White 1802 | A. Schulman Europe | mMDPE | ICORENE® |
| Dow Corning® C6-150 | Dow Corning Corporation | Silicone | Dow Corning® |