ULTEM™ 2210F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8hz5GQ_ULTEM-2210F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2210. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.50 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.55 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6500 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 17.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 210 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 205 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 223 | °C | ISO 306/A50 |
| -- | 212 | °C | ISO 306/B50 |
| -- | 218 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.5E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.28 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 34 | kV/mm | |
| 1.60 mm, in Oil | 26 | kV/mm | |
| 3.20 mm, in Oil | 16 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.10 | ||
| 60 Hz | 3.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| 1 MHz | 2.5E-3 | ||
| 2.45 GHz | 4.9E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 150 | V | |
| Solution B | 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 46 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 120 | °C | |
| Rear Temperature | 350 to 400 | °C | |
| Middle Temperature | 360 to 410 | °C | |
| Front Temperature | 370 to 420 | °C | |
| Nozzle Temperature | 360 to 410 | °C | |
| Processing (Melt) Temp | 370 to 410 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ K365GM | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| BESTPOLUX PCA85/01 | Triesa Plastics | PC+ABS | BESTPOLUX |
| Durethan® DP 2325 H3.0 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |
| Lucky Enpla LGF5408 | Lucky Enpla Co LTD | Nylon 6 | Lucky Enpla |
| Lupox® HV1010 | LG Chem Ltd. | PBT | Lupox® |