Lupoy® GP5008BFH
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8hb1gl_Lupoy-GP5008BFH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Flame Retardance, High Flow, Heat Resistant, High Impact Application E&E(Housing) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 54.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 80 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 123 | °C | ASTM D648 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 70.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.0196 to 0.0588 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM A3 MF PRTA010 PR304 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Homopolymer | Tenopom® POM |
| Comco PA 6/12 G | Comco-Plastic GmbH | Nylon 6/12 | Comco |
| Ferro PP LPP40BD05WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| KOPA® KN333G30BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| KOCETAL® CF704 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |