Terluran® GP-25
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8hZ4xz_Terluran-GP-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran GP-25 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.95 | % | |
| Equilibrium, 23°C, 50% RH | 0.24 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 99.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 44.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.4 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 12 | % | ISO 527-2 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 90 | kJ/m² | |
| 23°C | 130 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 22 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 15 | YI | DIN 6167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ GRCH24ST8 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Dryflex® WS 35M200 | ELASTO | TPE | Dryflex® |
| Geon™ Vinyl Flexible XV3900 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| HiFill® PA6/6 GF30 RM-1 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hyundai EP Breathable AT880H/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |