FRblend® PC-1303
| Category: | PC , Polycarbonate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8hPb3r_FRblend-PC-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PC-1303 is 10% glass fiber reinforced flame retardant polycarbonate compound complys with UL 94 V-0 rating at 1.6 mm thickness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 143 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4009EPG15 | POLYROCKS CHEMICAL CO., LTD | Nylon 6 | PONYL |
| TOTAL Polypropylene Lumicene® MR 2002 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Estane® ETE 60DS3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Karina WHITE PVC COMPOUND -E 806-10/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLIGOM R/75 G | Crosspolimeri S.p.A. | EPDM | POLIGOM |