Zytel® FE5382 BK276
| Category: | Nylon 612 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8flqSh_Zytel-FE5382-BK276.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced Polyamide 612 Developed for Electrical and Electronics Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Flow : 3.20 mm | 0.30 | -- | % | Internal Method |
| Across Flow : 3.20 mm | 1.0 | -- | % | Internal Method |
| Across Flow | 0.90 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 1.8 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.70 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9800 | -- | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break | 170 | -- | MPa | ISO 527-2 |
| 23°C | -- | 131 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break, 23°C | -- | 3.0 | % | ASTM D638 |
| Break | 2.5 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | -- | 6210 | MPa | ASTM D790 |
| -- | 8400 | -- | MPa | ISO 178 |
| Flexural Strength (23°C) | -- | 193 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 10 | -- | kJ/m² | |
| 23°C | 12 | -- | kJ/m² | |
| Notched Izod Impact | ||||
| 23°C | -- | 110 | J/m | ASTM D256 |
| -40°C | 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | 11 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | -- | 960 | J/m | ASTM D4812 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 216 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.12 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2130 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.26 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V97B | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| RTP 4091 | RTP Company | PPA | RTP |
| Santoprene™ 101-55W255 | ExxonMobil Chemical | TPV | Santoprene™ |
| FHR Polypropylene P4G4Z-011 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| King Pearl® G-L | Loyal Chemical | PS (EPS) | King Pearl® |