Stanyl® ForTii™ F31
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® ForTii™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8fScvv_Stanyl-ForTii-F31.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® ForTii™ F31 is a Polyamide 4T (Nylon 4T) material filled with 35% glass\mineral. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® ForTii™ F31 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.52 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.3 | 1.3 | % | ISO 527-2 |
| Flexural Modulus | 12000 | 12000 | MPa | ISO 178 |
| Flexural Stress | 165 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 295 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 325 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 4.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength | 33 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.400 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 320 to 330 | °C | |
| Middle Temperature | 325 to 335 | °C | |
| Front Temperature | 330 to 335 | °C | |
| Nozzle Temperature | 330 to 335 | °C | |
| Processing (Melt) Temp | 330 to 340 | °C | |
| Mold Temperature | 100 to 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 to 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1269A | Teknor Apex Company | TPE | Telcar® |
| SOLPLAST TC 4000C | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| LUVOCOM® 50/TF/15/GY04 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Sylvin 8225-60FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ GL004 compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |