MAGNUM™ 342 EZ
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ewf0z_MAGNUM-342-EZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 342 EZ ABS resin is a medium impact, high flow, low gloss resin often used in automotive applications. Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165°F to 190°F are available. Available primarily as natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 22.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded 3 | 1790 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20 mm, Injection Molded | 41.4 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2 5 |
| Tensile Elongation | |||
| Yield, 3.20 mm, Injection Molded | 3.0 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 6 |
| Nominal strain at break | > 50 | % | ISO 527-2 7 |
| Flexural Modulus 8(3.20 mm, Injection Molded) | 2000 | MPa | ASTM D790 |
| Flexural Strength 9(3.20 mm, Injection Molded) | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 10 | ||
| -30°C | 8.00 | kJ/m² | |
| 23°C | 16.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 11 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -18°C, 3.20 mm, Injection Molded | 80 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 160 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, 3.20 mm, Injection Molded, Peak Energy | 32.8 | J | |
| 23°C, 3.20 mm, Injection Molded, Total Energy | 42.9 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.6 | °C | ASTM D648 |
| 0.45 MPa | 89.0 | °C | ISO 75-2 12 |
| 1.8 MPa, Unannealed | 76.7 | °C | ASTM D648 |
| 1.8 MPa | 80.0 | °C | ISO 75-2 13 |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525 14 |
| 50°C/h, B (50N) | 94.0 | °C | ISO 306 15 |
| CLTE - Flow | 7.8E-5 | cm/cm/°C | ISO 11359-2 16 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 232 to 246 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 1.0 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Method I (3 point load), 2.0 mm/min |
| 9 . | Method I (3 point load), 2.0 mm/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Rate B (120°C/h), Loading 1 (10 N) |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3495 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Clariant Nylon 6/6 66G33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| CONAP® CE-2290 | Cytec Industries Inc. | Acrylic, Unspecified | CONAP® |
| Sylvin 7840-70 Red 6275 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BM 240 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |