Leona™ 90G60
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8egM3E_Leona-90G60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 90G60 is a Polyamide 66 (Nylon 66) product filled with 60% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 90G60 include automotive, construction applications and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.71 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.0 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 95 | 88 | ||
| R-Scale | 120 | 117 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 18200 | 13700 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 189 | 138 | MPa | ISO 527-2 |
| -- | 190 | 148 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.0 | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 16000 | 12900 | MPa | ASTM D790 |
| 23°C | 15800 | 12200 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 300 | 234 | MPa | ASTM D790 |
| 23°C | 324 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 56 | 54 | kJ/m² | ISO 179 |
| Notched Izod Impact | 95 | 100 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Specific Heat | 1840 | -- | J/kg/°C | |
| Thermal Conductivity | 0.30 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 475 | -- | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3401-3 | RTP Company | LCP | RTP |
| RAMOFIN PPH308G6 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| NYLOY® UB-0010N-V G55L2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Grilamid® 2D 25 W 20 X nat | EMS-GRIVORY | Nylon 612 | Grilamid® |
| INELEC ABSSS15 | Infinity LTL Engineered Compounds | ABS | INELEC |