Diamond ABS VP33 Black 1402
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8eNMNU_Diamond-ABS-VP33-Black-1402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diamond ABS VP-33 is a flame retardant (non-PBBE additives). Excellent moldability and good toughness. UL94 V-0 @ 1/16" (1.5mm). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (Injection Molded) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Injection Molded 2 | 41.4 | MPa | |
| Break, 23°C, 3.18 mm, Injection Molded 3 | 33.8 | MPa | |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm, Injection Molded | 2.3 | % | |
| Break, 23°C, 3.18 mm, Injection Molded | 9.6 | % | |
| Flexural Modulus - Tangent 5(Injection Molded) | 2340 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.18 mm, Injection Molded | 71.1 | °C | ASTM D648A |
| 1.8 MPa, Annealed, 3.18 mm | 92.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.3 | °C | ASTM D1525 6 |
| RTI Elec (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 171 to 182 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 199 to 216 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 199 to 221 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I |
| 4 . | Type I |
| 5 . | Method I (3 point load), Type I, 1.3 mm/min |
| 6 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 1837 MAS081 | Covestro - Polycarbonates | PC | Makrolon® |
| RTP 4703 | RTP Company | PTT | RTP |
| REVOLVE® M-776 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| UNITEM® Sfx-0149 | Nytef Plastics, Ltd. | PEI | UNITEM® |
| LEXAN™ EXRL2032 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |