LNP™ LUBRICOMP™ IFL34 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8dLrX0_LNP-LUBRICOMP-IFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IFL34 is a compound based on Nylon 6/12 resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IFL-4034 Product reorder name: IFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Flow : 24 hr | 0.41 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 7100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 116 | MPa | ASTM D638 |
| Yield | 121 | MPa | ISO 527-2 |
| Break | 116 | MPa | ASTM D638 |
| Break | 121 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.1 | % | ASTM D638, ISO 527-2 |
| Break | 3.1 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 6100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.47 | ||
| Wear Factor - Washer | 18.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 9.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 930 | J/m | ASTM D4812 |
| 23°C 3 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.70 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 212 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 195 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® A-331C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Armlen® PP TM 30.1 | Poly Plastic | PP, Unspecified | Armlen® |
| Flexirene® FG 23 F | Versalis S.p.A. | LLDPE | Flexirene® |
| ELIX™ ABS H702 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| POLYFORT® FPP 1876 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |