Complet® LGF40-PA66 MT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PlastiComp, Inc. |
| Trademark: | Complet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8cwDQT_Complet-LGF40-PA66-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Complet®LGF40-PA66 MT is a polyamide 66 (nylon 66) product, which contains 40% long glass fibers as filler. It is available in North America, Europe or Asia Pacific. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 296 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 510 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 246 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 282 - 299 | °C | |
| Middle Temperature | 288 - 304 | °C | |
| Front Temperature | 293 - 310 | °C | |
| Nozzle Temperature | 288 - 304 | °C | |
| Processing (Melt) Temp | 293 - 310 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 30 - 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Injection speed: 2 to 3 in/secInjection pressure: medium to maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC2-1090U | Spartech Polycom | PS (HIPS) | Spartech |
| Xuchuan 2001/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| GERMAMID 6 HVX | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| ESTOPLAST EP 4125GY81 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7403WZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |