Halene H P5300
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8cOHRX_Halene-H-P5300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
P5300 is a pipe grade HDPE, produced by the Mitsui CX Process. This resin is recommended for PE 112 high-pressure pipe applications. P5300 combines exceptional processability with high creep resistance, high ESCR and excellent mechanical properties. P5300 has a MRS 11.2 MPa according to ISO 9080 and is designated PE 112 according to ISO 12162:1995. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 26.0 | MPa | |
| Break, Compression Molded | 41.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, Compression Molded | 8.0 | % | |
| Break, Compression Molded | 1000 | % | |
| Flexural Modulus (Compression Molded) | 1000 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 270 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 3 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Oxidation Induction Time | > 30 | min | ASTM D3895 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Critical Pressure for Crack Propagation (0°C) | > 1.20 | MPa | ISO 13477 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 to 220 | °C | |
| Cylinder Zone 2 Temp. | 160 to 220 | °C | |
| Cylinder Zone 3 Temp. | 160 to 220 | °C | |
| Cylinder Zone 4 Temp. | 160 to 220 | °C | |
| Cylinder Zone 5 Temp. | 160 to 220 | °C | |
| Die Temperature | 220 | °C |
| Note Message | |
|---|---|
| 1 . | 27°C |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4450 G5 | BASF Corporation | PBT | Ultradur® |
| Andur AL 90 AP/Curene® 89 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| CP PRYME® Nylon 6 N140MGHSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Monprene® MP-3020 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| LEXAN™ 221R resin | SABIC Innovative Plastics | PC | LEXAN™ |