MAGNUM™ 3904 Smooth LP
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8bfGaR_MAGNUM-3904-Smooth-LP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3904 is an extrusion / thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. With its ultra-low particulate content, this grade is an addition to the " Smooth Series" and features a lower plate (LP) out content. This results in a superior surface finish in which the plate out build-up on the extruder roll stack is reduced significantly. This new grade enables customers to produce parts with both outstanding aesthetics and surface cleanness at lower total cost. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.7 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.10 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1820 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 37.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 39.0 | MPa | ISO 527-2/100 |
| Tensile Strain | |||
| Yield, 3.20 mm, Injection Molded | 2.6 | % | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 2.8 | % | ISO 527-2/100 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Stress | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7530 GK 10 GF 20 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| GAPEX® HP RPP10EB90AL | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| Lucent PC PC-1410FD | Lucent Polymers, Inc. | PC | Lucent PC |
| Petrotene® PP A3 C35 BRC0001 PH383 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Durethan® BM 240 H2.0 901510 | LANXESS Corporation | Nylon 6 | Durethan® |