Starglas OC004
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starglas |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8arTIF_Starglas-OC004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starglas OC004 is a 20 % Carbon Fiber Reinforced PPS Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.15 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 144 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 15100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 194 | MPa | |
| -- 4 | 193 | MPa | |
| Flexural Strain at Break 5 | 1.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 275 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 235 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 305 to 315 | °C | |
| Middle Temperature | 320 to 330 | °C | |
| Front Temperature | 330 to 345 | °C | |
| Processing (Melt) Temp | 315 to 320 | °C | |
| Mold Temperature | 140 to 165 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 9608 | Chevron Phillips Chemical Company LLC | HDPE | MarFlex® |
| Clariant Nylon 6/6 PA-131 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| KRATON® D1162 P | Kraton Polymers LLC | SIS | KRATON® |
| OPTUM® DPP30WF08AL | Ferro Corporation | Polyolefin, Unspecified | OPTUM® |
| LEXAN™ FXD1414T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |