Infino WR-7000P
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8aelnK_InfinoWR7000P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WR-7000P is an acrylonitrile-styrene-acrylate PC (ASA PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 - 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 111 | ASTM D785 | |
| R scale | 111 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 58.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 54.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 60 | % | ASTM D638 |
| Fracture | 60 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 80.0 | MPa | ASTM D790 |
| -- 8 | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 43 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 150 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 450 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 140 | J/m | ASTM D256 |
| 23°C 10 | 42 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 116 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 115 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 114 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA TW15 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| UBE Polyethylene F222 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| AMTOPP PCS80 | Inteplast Group | PP, Unspecified | AMTOPP |
| Elastocon® 8150B | Elastocon TPE Technologies | TPE | Elastocon® |
| LEXAN™ MPX1 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |