InnoClear™ OC-7085
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoClear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8a7xiN_InnoClear-OC-7085.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OC-7085 is a water-clear, semi-rigid polyurethane formulated for room temperature hand batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI The unique chemistry of OC-7085 imparts excellent optical clarity as well as UV stability. This material has been specially formulated for mass castings into either tin or platinum silicone molds. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.10 | g/cm³ | |
| Hardener | 1.10 | g/cm³ | |
| Base Resin | 1.13 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 95.0 | °C | |
| 1.8 MPa, Unannealed | 91.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 59 Mix Ratio by Weight: 57 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 960 to 1400 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Exotherm - 200g mass | 52 | °C |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.45 | Pa·s | |
| 25°C 2 | 0.65 | Pa·s | |
| 25°C 3 | 1.3 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 80 to 1.2E+2 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Modulus | 1830 | MPa | ASTM D638 |
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation at Break | 8.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 PA1212C-01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| AIE PA6 50G6ST | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| Formolon® 608 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Hylon® N2040MGHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| KEBAFLEX® S 35 A.01 | BARLOG plastics GmbH | TES | KEBAFLEX® |