VECTRA® MT1300
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ZDv01_VECTRA-MT1300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced Vectra grade suitable for extrusion. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant Celanese has established at the FDA a drug master file (DMF no.8468) and a Device Master File (MAF no.315) for Vectra MT1300. These are to assist our customers with their end use FDA petitions. Vectra MT1300 has been tested and complies with USP Class VI. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 182 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/1A/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9000 | MPa | ISO 899-1 |
| 1000 hr | 6600 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 9100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 158 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m² | ISO 179/1eU |
| 23°C | 270 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 95 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 250 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 187 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 94.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Melting Temperature 1 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 47 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.20 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.016 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 285 - 295 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 285 to 295°CZone 4 Temperature: 285 to 295°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-1042 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Sylvin 8874-81C NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CLEAREN 530L | Denka Company Limited | SBC | CLEAREN |
| LNP™ STAT-KON™ DX98477 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| POLYFLAM® RIPP 2000 S | A. Schulman Europe | PP Copolymer | POLYFLAM® |