RTP 2203 LF TFE 20
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ZAGyx_RTP-2203-LF-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 0.30 | % | ASTM D955 |
| 6.35mm, injection molding | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 10300 | MPa | ASTM D638 |
| Tensile Strength | 141 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 3.5 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 8270 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 343 - 388 | °C | |
| Middle Temperature | 343 - 388 | °C | |
| Front Temperature | 343 - 388 | °C | |
| Mold Temperature | 163 - 218 | °C | |
| Injection Pressure | 83.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 126218 A | RTP Company | PLA | RTP |
| Sarlink® TPE EE-2270N-01 | Teknor Apex Company | TPE | Sarlink® TPE |
| Daelim Po1y® LL-05S | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| ESTASTIR HI 0508 V0 | Cossa Polimeri S.r.l. | PS (HIPS) | ESTASTIR |
| Karina BLACK PVC COMPOUND 710-48/1-O-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |