DOW™ LLDPE DNDA-7144 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8YRh6o_DOW-LLDPE-DNDA-7144-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOW DNDA-7144 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL™ PE Process Technology and is intended for use in injection molding applications such as large industrial containers and trash cans. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 20.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 11.7 | MPa | ASTM D638 |
| Fracture | 7.58 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 386 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 42.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 108 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Triapol® Blends C3 K46 PRTA011 BS310 MSP | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| Nylene® BS-640-A | Custom Resins Group | Nylon 6 | Nylene® |
| Borealis PP RA130E-6034 | Borealis AG | PP Random Copolymer | Borealis PP |
| LUVOCOM® 20/SCF/30 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Polifor® C 8 GRIGIO 7222 | SO.F.TER. SPA | PP Copolymer | Polifor® |