LNP™ STAT-KON™ DE0049P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8YIsWl_LNP-STAT-KON-DE0049P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DE0049P is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1004 EP FR Product reorder name: DE0049P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.56 | % | ISO 294-4 |
| Flow : 24 hr | 0.14 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16500 | MPa | ASTM D638 |
| -- | 16000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 137 | MPa | ASTM D638 |
| Break | 132 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 0.90 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12400 | MPa | ASTM D790 |
| -- | 13200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 219 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 139 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5206-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRIREX® Compound 3500G30 | Samyang Corporation | PC | TRIREX® Compound |
| Westlake LDPE EP310 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Latiohm 75/4-08 PD01 G/30 | LATI S.p.A. | PBT | Latiohm |
| Sylvin 5222-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |