Electrafil® J-1200/CF/10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8YAWIC_Electrafil-J-1200-CF-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-1200/CF/10 is an acrylonitrile butadiene styrene (ABS) product, which contains a filler of 10% carbon fiber reinforcement. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-1200/CF/10 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7580 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6890 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | 50 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257: 1E2-1E3 ohms/sqVolume Resistivity, ASTM C611: 10-100 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 87.8 | °C | |
| Drying Time | 2.0 - 16 | hr | |
| Rear Temperature | 216 - 232 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 232 - 260 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPAMID 66 2525 V0 | Vamp Tech | Nylon 66 | VAMPAMID |
| Next Nylon 66 Industrial Series PX-02NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Industrial Series |
| Badaflex® TPE-S 40A 1462 AB transparent | Bada AG | SEBS | Badaflex® |
| Sinpolene TPP6520 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | SINPOLENE |
| Dryflex® SE 65A001 | ELASTO | TPE | Dryflex® |