Texin® 950LW
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Texin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Y2k7r_Texin-950LW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Texin 950LW resin is an aromatic polyether-based thermoplastic polyurethane. It can be processed by injection molding, extrusion or blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.54mm | 0.80 | % | ASTM D955 |
| Transverse flow : 2.54mm | 0.80 | % | ASTM D955 |
| Vertical flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 114 | MPa | ASTM D790, ISO 178 |
| Taber Abrasion Resistance | |||
| 1000 Cycles, 1000g, H-18 wheel | 75.0 | mg | ISO 4649 |
| 1000 Cycles, 1000g, H-18 wheel | 75.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| 100% strain | 14.5 | MPa | ASTM D412, ISO 37 |
| 300% strain | 30.3 | MPa | ASTM D412, ISO 37 |
| Tensile Strength (Yield) | 49.7 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation (Break) | 460 | % | ASTM D412, ISO 37 |
| Tear Strength | |||
| -- 1 | 131 | kN/m | ASTM D624 |
| -- | 130 | kN/m | ISO 34-1 |
| Compression Set 2 | ASTM D395B, ISO 815 | ||
| 23°C, 22 hr | 15 | % | ASTM D395B, ISO 815 |
| 70°C, 22 hr | 40 | % | ASTM D395B, ISO 815 |
| Bayshore Resilience | 35 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ISO 306/50, ASTM D1525 3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 93.0 - 104 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 196 - 207 | °C | |
| Middle Temperature | 199 - 210 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Nozzle Temperature | 202 - 213 | °C | |
| Processing (Melt) Temp | 202 - 216 | °C | |
| Mold Temperature | 15.0 - 40.0 | °C | |
| Injection Pressure | 41.4 - 103 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | < 5.52 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Cushion | < 3.18 | mm |
| Injection instructions |
|---|
| Hold Pressure: 60 to 80% of Injection Pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.0 - 104 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 196 | °C | |
| Cylinder Zone 2 Temp. | 193 - 207 | °C | |
| Cylinder Zone 3 Temp. | 193 - 207 | °C | |
| Melt Temperature | 199 - 213 | °C | |
| Die Temperature | 193 - 213 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Post-cured 16 hr at 230°F |
| 3 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP PPSU 1000 | Quadrant Engineering Plastic Products | PPSU | Quadrant EPP |
| Estane® CP80AS2 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| EPO-TEK® H67MP-GB | Epoxy Technology Inc. | Epoxy | EPO-TEK® |