SIBUR Synthetic Rubber SBR-1712 HI-AR Grade A
| Category: | SBR, Unspecified , Styrene Butadiene Rubber |
| Manufacturer: | SIBUR, LLC |
| Trademark: | SIBUR Synthetic Rubber |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8X9BhV_SIBUR-Synthetic-Rubber-SBR-1712-HI-AR-Grade-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Oil-extended styrene butadiene synthetic rubber SBR-1712 HI-AR is essentially a styrene (23.5%) and butadiene (76.5%) copolymer obtained by emulsification method with the use of resin/fatty soaps. The copolymer is filled with oil HI-AR. Product characteristics: Appearance - bale of dark-brown color; weight of a bale - (30 ± 1) kg; packing - a plastic container; shelf life - one (1) year since the date of manufacture |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 46 to 52 | MU | ASTM D1646 |
| Bound Styrene | 22.5 to 24.5 | % | Internal Method |
| Antioxidant Additive - VS-1 | 0.30 to 0.70 | % | Internal Method |
| Ash Content | < 0.60 | % | ASTM D5667 |
| Oil Content 1 | 26 to 29 | % | ASTM D5774 |
| Organic Acid | 4.2 to 5.8 | % | ASTM D5774 |
| Soap - Organic Acid | < 0.30 | % | ASTM D5774 |
| Solvent Content - extract | 29 to 35 | % | Internal Method |
| Volatile Matter | < 0.60 | % | ASTM D5668 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rheometer MDR 2000 2 | ASTM D5289 | ||
| Maximum Torque (MH) : 160°C | 12.0 to 18.5 | dNm | |
| Minimum Torque (ML) : 160°C | 1.40 to 3.00 | dNm | |
| Prevulcanization start time (ts1) : 160°C | 3.2 to 6.5 | min | |
| Time to 50% vulcanization (T'50) : 160°C | 6.5 to 10.5 | min | |
| Time to 90% vulcanization (T'90) : 160°C | 12.0 to 18.5 | min |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | > 9.80 | MPa | ASTM D3185 |
| Tensile Strength (Yield) | > 18.0 | MPa | ASTM D3185 |
| Tensile Elongation (Break) | > 380 | % | ASTM D3185 |
| Note Message | |
|---|---|
| 1 . | Oil type: HI-AR |
| 2 . | deformation of 0.5°, MH at 30 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S HS 105 M NAT | Radici Plastics | Nylon 6 | Radilon® |
| XENOY™ 1102 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Grilamid® LV-2H | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LTP ZW-3125 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |
| LEXAN™ XHT3141 resin | SABIC Innovative Plastics | PC | LEXAN™ |