INEOS PP 400-GA05
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8X4Nvh_INEOS-PP-400-GA05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
400-GA05 is a general purpose high impact copolymer for injection moulding applications. It offers a superior balance of stiffness and impact strength as compared to competitive impact copolymers of similar melt flow rate. Applications
Benefits and Features
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.5 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 6.5 | kJ/m² | |
| 23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 86.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 152 | °C | ISO 306/A |
| Peak Melting Temperature | 164 | °C | ASTM D3417 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LLB1918F | Trademark Plastics Corporation | LLDPE | Trademark PE |
| TRIREX® Compound 3025GRU30 | Samyang Corporation | PC | TRIREX® Compound |
| ADEKA ED-529 | Adeka Corporation | Epoxy | ADEKA |
| Grilon® BGM-40 X | EMS-GRIVORY | Nylon 6 | Grilon® |
| ULTEM™ CRS5201 resin | SABIC Innovative Plastics | PEI | ULTEM™ |