NYLOY® PG-0020N
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Vz3nC_NYLOY-PG-0020N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® PG-0020N is a Polypropylene material filled with 20% glass fiber. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.891 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.84 | % | |
| Across Flow | 1.1 | % | |
| Ash Content | 20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 95 | ASTM D785 | |
| R-Scale | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 66.7 | MPa | ASTM D638 |
| -- | 72.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.0 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3960 | MPa | ASTM D790 |
| -- | 4100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 92.2 | MPa | ASTM D790 |
| -- | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 61 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 150 | °C | |
| 1.8 MPa, Unannealed | 138 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-137B | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Tenogel® ABS A3 LF NTLA010 AB348 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| Latamid SP2 H2 G/45 | LATI S.p.A. | Nylon 612 | Latamid |
| LNP™ THERMOCOMP™ RX05494 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Petrothene® GA502022 | LyondellBasell Industries | LLDPE | Petrothene® |