Akulon® K224-G6U
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8VMuQ9_Akulon-K224-G6U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® K224-G6U is a Polyamide 6 (Nylon 6) material filled with 33% glass fiber. It is available in North America. Primary attribute of Akulon® K224-G6U: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 9200 | -- | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 15 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 70 | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 20.0 | ||
| 1 MHz | 3.30 | 5.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.30 | ||
| 1 MHz | 0.015 | 0.12 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HCA-352S | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| Ravathane R210D52UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| SCHULAMID® 612 GF 30 H | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| SUMIKASUPER® LCP E5204L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| ESTABIO EX 03120 B | Cossa Polimeri S.r.l. | Copolyester | ESTABIO |