LNP™ THERMOCOMP™ OF008H compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8V6GGq_LNP-THERMOCOMP-OF008H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008H is a compound based on PPS - Linear containing 40% Glass Fiber. Characteristics of this grade are: Healthcare. Also known as: LNP* THERMOCOMP* Compound OF-1008 HC Product reorder name: OF008H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 | % | |
| Across Flow : 24 hr | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 14100 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 140 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 14200 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 234 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.50 | ||
| Wear Factor - Washer | 373 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 264 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.450 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-305 (Comp) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| Titalon® 1100ST | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Trexlink™ 4760 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Americas Styrenics EA6740 | Americas Styrenics LLC | PS (HIPS) | Americas Styrenics |
| LUVOCOM® 1850-7692 VP | Lehmann & Voss & Co. | PBT | LUVOCOM® |