LNP™ THERMOCOMP™ AF004 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8UM7z6_LNP-THERMOCOMP-AF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF004 is a compound based on ABS resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound AF-1004 Product reorder name: AF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.24 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.24 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.39 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6180 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 78.6 | MPa | ASTM D638 |
| Break | 81.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.2 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6150 | MPa | ASTM D790 |
| -- | 5860 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 130 | MPa | ASTM D790 |
| -- | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 3 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.1 | J | ASTM D3763 |
| -- | 3.11 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 93.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 74-8208-F | Teknor Apex Company | PVC, Flexible | APEX® |
| Lion Idemitsu Composites PPS G131J1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Sylvin 83014-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8205-85UV Brown 7485 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SEQUEL® 1480 PUV NATRL | LyondellBasell Industries | TPO (POE) | SEQUEL® |